Semiconductor Hot isostatic pressing(HIP) Zirconia oxide surface grinding 1. Enhancement of Surface Quality, well surface roughness after rough cut. 2. Brittle Edge is less than 0.005mm (inspected by optical microscope. HIT Achievements HIT Highlights & Comparison Industry Application Difficulties in Machining Back to list Hot isostatic pressing(HIP) Zirconia oxide surface grinding - HIT Achievements Hot isostatic pressing(HIP) Zirconia oxide surface grinding: Picture of work piece: Measuring data of surface roughness: The high frequency vibrations of ultrasonic machining can subtly remove excessive materials and prevent micro-crack in the structure. Thus, ultrasonic machining is proven effective in enhancing surface quality. Inspection of surface quality: The performace shows that after using HIT ultrasonic machining module, the surface becomes uniformed and the brittle edge can be less than 0.005mm inspected by optical microscope. Machining data table: Highlights of HIT Ultrasonic Machining Module: Enhancement of Surface Quality, well surface roughness after rough cut. Brittle Edge is less than 0.005mm (inspected by optical microscope. Hot isostatic pressing(HIP) Zirconia oxide surface grinding - HIT Highlights & Comparison Hot isostatic pressing(HIP) Zirconia oxide surface grinding - Industry Application Hot isostatic pressing(HIP) Zirconia oxide surface grinding - Difficulties in Machining